deoxidizing
英
美
网络 脱氧; 去氧
双语例句
- We applied the thermodynamic principle to analyze the thermodynamic condition for deoxidizing the oxide of Si-Mn. According to our result, we designed a new technigue, the surface of water-atomized Si-Mn steel powder deoxidized in pure N2 with thermoset resin.
本文用热力学原理分析了Si-Mn氧化物还原的热力学条件，并根据其热力学分析结果，对水雾化Si-Mn钢粉采用热塑性树脂涂层，在高纯氮气氛中进行脱氧的新工艺研究。 - A new regenerative magnesium deoxidizing has been designed by utilizing the technology of high temperature combustion technology, which has been developed in the recent years.
分析了传统金属镁还原炉的问题所在，利用近年来发展起来的高温空气燃烧技术，设计开发了新型蓄热式金属镁还原炉。 - The size of deoxidizing products increases with the increased degree of supersaturation of deoxidizing elements;
脱氧产物尺寸随脱氧元素过饱和度增加而增加； - Third the influence of the liquid steel flowing on the eliminating of firstly deoxidizing products is studied;
研究了钢液流动现象对一次脱氧去除的影响； - Metallurgical Problems in Heat-Resistance Steel Composition Design of Deoxidizing Ladle for Refining Mg
炼镁还原罐用耐热钢成份设计中的金属学问题 - The composition of the secondly and thirdly deoxidizing products can be controlled through controlling the content of aluminum and calcium of the strong deoxidizing elements, making them have good distortion ability in hot work.
二次和三次脱氧产物的成分可以通过控制钢液中强脱氧元素铝和钙的含量来控制，使它们具有良好的热加工变形能力。 - The results are concluded as follows: All of the samples have different levels of deoxidizing ability.
结果如下：总还原力测定结果：所有样品都表现出了不同程度的还原能力。 - The separation process about deoxidizing stove tail gas in the modified siemens arts and crafts in polycrystalline silicon production was improved.
对改良西门子法多晶硅生产中尾气分离工艺进行了改进。 - Preparation of high-concentration sulfur dioxide from deoxidizing phosphogypsum with compound reducing agent
硫脲作还原剂制备二氧化锰及其电化学性能复合还原剂还原分解磷石膏制取高浓度二氧化硫 - The preparation of ultrafine WO_3 powders and the deoxidizing and carbonizing of WO_3 to WC were studied. Well abrasive resistant metal composite coating strengthened by ultrafine WC particles was prepared by flame thermal spray method and abrasive wear property was studied.
本文探索了超细WO3粉的制备及其还原碳化为WC粉的方法，采用火焰热喷涂工艺，制备了耐磨性能较好的超细WC陶瓷&金属复合涂层，并研究了涂层的耐磨性能。